White fused alumina is widely used as a raw material of ceramics vitrified tools and resin-bonded grinding tools, but also used as grinding, polishing, blasting, precision casting and high-class refractories.
White Fused Alumina is cooling from electrically fused in an arc furnace from industrial alumina powder which is as the main raw material at high temperature above 2000℃. With crushing, shaping, magnetic sorting, it has been sieved into a variety of grit sizes. White fused alumina is widely used as a raw material of ceramics vitrified tools and resin-bonded grinding tools, but also used as grinding, polishing, blasting, precision casting and high-class refractories. WA as the code name, its Chinese chemical standard is consistent with international standard. We have majority of export and some quantity for domestic trade.
Grit | Oversized Grain | Big Grain | Basic Grain | Mangcorn |
Fine Grain
|
||||||||||
Sieve Size | Oversize | Sieve Size | Oversize≤ | Sieve Size |
Oversize ≥ |
Sieve Size |
Oversize ≥ |
Sieve Size |
Undersize ≤ |
||||||
mm | μm | Mass Ratio % | mm | μm | Mass Ratio % | mm | μm | Mass Ratio % | mm | μm | Mass Ratio % | mm | μm | Mass Ratio % | |
F4 | 8.00 | — | 0 | 5.60 | — | 20 | 4.75 | — | 40 | 4.75 4.00 | — | 70 | 3.35 | — | 3 |
F5 | 6.70 | — | 0 | 4.75 | — | 20 | 4.00 | — | 40 | 4.00 3.35 | — | 70 | 2.80 | — | 3 |
F6 | 5.60 | — | 0 | 4.00 | — | 20 | 3.35 | — | 40 | 3.35 2.80 | — | 70 | 2.36 | — | 3 |
F7 | 4.75 | — | 0 | 3.35 | — | 20 | 2.80 | — | 40 | 2.80 2.36 | — | 70 | 2.00 | — | 3 |
F8 | 4.00 | — | 0 | 2.80 | — | 20 | 2.36 | — | 45 | 2.36 2.00 | — | 70 | 1.70 | — | 3 |
F10 | 3.35 | — | 0 | 2.36 | — | 20 | 2.00 | — | 45 | 2.00 1.70 | — | 70 | 1.40 | — | 3 |
F12 | 2.80 | — | 0 | 2.00 | — | 20 | 1.70 | — | 45 | 1.70 1.40 | — | 70 | 1.18 | — | 3 |
F14 | 2.36 | — | 0 | 1.70 | — | 20 | 1.40 | — | 45 | 1.40 1.18 | — | 70 | 1.00 | — | 3 |
F16 | 2.00 | — | 0 | 1.40 | — | 20 | 1.18 | — | 45 | 1.18 1.00 | — | 70 | — | 850 | 3 |
F20 | 1.70 | — | 0 | 1.18 | — | 20 | 1.00 | — | 45 | 1.00 — | 850 — | 70 | — | 710 | 3 |
F22 | 1.40 | 0 | 1.00 | — | 20 | — | 850 | 45 | — | 850 710 | 70 | — | 600 | 3 | |
F24 | 1.18 | — | 0 | — | 850 | 25 | — | 710 | 45 | — | 710 600 | 65 | — | 500 | 3 |
F30 | 1.00 | — | 0 | — | 710 | 25 | — | 600 | 45 | — | 600 500 | 65 | — | 425 | 3 |
F36 | — | 850 | 0 | — | 600 | 25 | — | 500 | 45 | — | 500 425 | 65 | — | 355 | 3 |
F40 | — | 710 | 0 | — | 500 | 30 | — | 425 | 40 | — | 425 355 | 65 | — | 300 | 3 |
F46 | — | 600 | 0 | — | 425 | 30 | — | 355 | 40 | — | 355 300 | 65 | — | 250 | 3 |
F54 | — | 500 | 0 | — | 355 | 30 | — | 300 | 40 | — | 300 250 | 65 | — | 212 | 3 |
F60 | — | 425 | 0 | — | 300 | 30 | — | 250 | 40 | — | 250 212 | 65 | — | 180 | 3 |
F70 | — | 355 | 0 | — | 250 | 25 | — | 212 | 40 | — | 212 180 | 65 | — | 150 | 3 |
F80 | — | 300 | 0 | — | 212 | 25 | — | 180 | 40 | — | 180 150 | 65 | — | 125 | 3 |
F90 | — | 250 | 0 | — | 180 | 20 | — | 150 | 40 | — | 150 125 | 65 | — | 106 | 3 |
F100 | — | 212 | 0 | — | 150 | 20 | — | 125 | 40 | — | 125 106 | 65 | — | 75 | 3 |
F120 | — | 180 | 0 | — | 125 | 20 | — | 106 | 40 | — | 106 90 | 65 | — | 63 | 3 |
F150 | — | 150 | 0 | — | 106 | 15 | — | 75 | 40 | — | 75 63 | 65 | — | 45 | 3 |
F180 | — | 125 | 0 | — | 90 | 15 | — | 75 63 | 40 | — | 75 63 53 | 65 | — | — | — |
F220 | — | 106 | 0 | — | 75 | 15 | — | 63 53 | 40 | — | 63 53 45 | 60 | — | — | — |
Code | Grit Size | Chemical Composition % | |
Al2O3≥ | Na2O≤ | ||
WA and WA-P |
F4 ~F80 P12~P80 |
99.10 | 0.35 |
F90~F150 P100~P150 |
99.10 | 0.40 | |
F180~F220 P180~P220 |
98.60 | 0.50 | |
F230~F800 P240~P800 |
98.30 | 0.60 | |
F1000~F1200 P1000~P1200 |
98.10 | 0.70 | |
P1500~P2500 | 97.50 | 0.90 |